Follow the following principles when welding:

1. The thicker the plate, the thicker the welding wire, the greater the power, the slower the wire feed speed.

2. The lower the power, the whiter the welding surface, the greater the power, the weld form color to black, at this time, single side forming.

3. The thickness of the welding wire should not be greater than the plate thickness to the plate thickness, the welding wire affects the fullness of the weld.

4. The thinner the wire, the lower the scan width.

Affected by different brands of lasers, the following laser proofing test is used in the following process, for reference only, and appropriate fine-tuning is required when using.

①RECI /MAX/JPT

②Argon gas

* About Carbon Steel

* About Stainless Steel

* About Aluminum

Aluminum process refer to stainless steel process, power can be increased by 20%-30%, in addition, there are differences in focus, need to be manually adjusted.

Reference: 0.5MM stainless steel negative Angle welding.

0.8 stainless steel welding wire, scanning speed 350, scanning width 2, peak power350, duty ratio100,frequency 2000.

The outgoing light penetrates the plate and deforms greatly, so we reduce the power treatment.

0.8 stainless steel welding wire, scanning speed 350, scanning width 2, peak power260, duty ratio100,frequency 2000.

The deformation is reduced, but the initial light is still easy to burn through, so we continue to reduce the power treatment.

0.8 stainless steel welding wire, scanning speed 350, scanning width 2, peak power200,, duty ratio100,frequency 2000.

The effect is as follows①, as shown in ②when the width is increased to 3.